Filter datasheet

Variants

Material data sheet

Steel grade

  • Imacro
Last revised: Tue, 07 Feb 2023 13:59:12 GMT

General Information

9259, also known as Imacro EL700, is a grade with a low carbon content which gives the steel a very good toughness in as rolled condition.

8302, also know as Imacro M, is a weldable quenched and tempered steel with good toughness. The structure in the hardened condition is lath martensite.

 

* Designation followed by "*" is not an official EN standard grade but named according to the rules in EN 10027.

M-Steel®

The basis for the concept is that non-metallic inclusions are modified and controlled with calcium treatment in a way to minimize tool wear and to maximize chip control in machining operations. Our M-Steel treatment can be applied to any steel grade. 

Other properties (typical values)

Youngs module (GPa)Poisson´s ratio (-)Shear module (GPa)Density (kg/m3)
210 0.3 80 7800
 Average CTE 20-300°C (µm/m°K) Specific heat capacity 50/100°C (J/kg°K) Thermal conductivity Ambient temperature (W/m°K) Electrical resistivityAmbient temperature (µΩm)
 12  460 - 480  40 - 45  0.20 - 0.25

Contact us

Would you like to know more about our offers? Don´t hesitate to contact us:

Via e-mail: info@ovako.com 

Via telephone: +46 8 622 1300

For more detailed information please visit http://www.ovako.com/en/Contact-Ovako/

  

 

Disclaimer

The information in this document is for illustrative purposes only. The data and examples are only general recommendations and not a warranty or a guarantee. The suitability of a product for a specific application can be confirmed only by Ovako once given the actual conditions.The purchaser of an Ovako product has the responsibility to ascertain and control the applicability of the products before using them. Continuous development may necessitate changes in technical data without notice. This document is only valid for Ovako material. Other material, covering the same international specifications, does not necessarily comply with the properties presented in this document.