General Information
Ovako 837 is a through hardening bearing steel that is mainly used for medium sized bearing rings, but can also be used for machine components that require high tensile strength and high hardness.
- 30 mm maximum wall thickness for through hardening
- Used for martensitic hardening
- Can be induction hardened
- Good machinability in soft annealed condition
- Machinable in hardened condition using hard-turning techniques (CBN tools)
- Very good dimension stability
837R - Bearing quality (BQ) variant
837S - Variant with a controlled high sulphur content for enhanced low speed machining
5625 / 837Z - A continous cast variant (BQ)
Similar designations
ASTM A485 grade B3, 100 CM 6
Other properties (typical values)
| Youngs module (GPa) | Poisson´s ratio (-) | Shear module (GPa) | Density (kg/m3) |
|---|
| 210 |
0.3 |
80 |
7800 |
| Average CTE 20-300°C (µm/m°K) | Specific heat capacity 50/100°C (J/kg°K) | Thermal conductivity Ambient temperature (W/m°K) | Electrical resistivityAmbient temperature (µΩm) |
|---|
| 12 |
460 - 480 |
40 - 45 |
0.20 - 0.25 |
Disclaimer
The information in this document is for illustrative purposes only. The data and examples are only general recommendations and not a warranty or a guarantee. The suitability of a product for a specific application can be confirmed only by Ovako once given the actual conditions.The purchaser of an Ovako product has the responsibility to ascertain and control the applicability of the products before using them. Continuous development may necessitate changes in technical data without notice. This document is only valid for Ovako material. Other material, covering the same international specifications, does not necessarily comply with the properties presented in this document.